Weak Rivets May Have Sped Sinking of Titanic

Pickens writes "Metallurgists studying the hulk of the Titanic argue that the liner went down fast after hitting an iceberg because the ship's builder used substandard rivets that popped their heads and let tons of icy seawater rush in. They say that better rivets would have probably kept the Titanic afloat long enough for rescuers to have arrived, saving hundreds of lives. The team collected clues from 48 Titanic rivets and found many riddled with high concentrations of slag, a glassy residue of smelting that can make iron brittle. To test whether this extra slag weakened the rivets, scientists commissioned a blacksmith to make rivets to the same specifications as those used to join steel plates in the hull of the Titanic. When the plates were bent in the laboratory, the rivet heads popped off at loads of about 4,000 kg. With the right slag content they should have held up to about 9,000 kg. Even a few failures because of flawed metal would have been sufficient to unzip entire seams, because as faulty rivets popped, more stress would have been placed on the good ones, causing them to break in turn. The shipbuilder, which is still in existence, denies it all."

Comments

How is this new information?

[Taelron]

Since the mid-90's there have been tons of BBC and Discovery Science and History channel specials on the Titanic and they ALL said the same thing, the shipyard used substandard metals in the rivett's to cut back on the cost of building the ship. And these same history shows all said the same thing, to much slag found in the rivets causing them to be extremely week and would pop with minimal, for its size, force.

Re:How is this new information?

[Kredal]

Tag "oldnews"

The article states that the rivets were first talked about in 1998, but the shipbuilder disagreed. Since then, more people have looked at the rivets, and they have all said the same thing. Rivets were bad, they failed under pressure, and the ship sank. The only reason this is "news" is because they found corroborating evidence in the shipbuilder's old documents.

Re:How is this new information?

[Tsu Dho Nimh]

During 1912-13 the Olympic returned to Harland & Wolff for six months safety rebuilding. The double bottom was extended up the sides to the waterline, full height bulkheads were fitted, as were additional lifeboats.

26 April 1999

[wombatmobile]

"Given the microstructure that we've seen, our best guess is that the rivets failed before the steel plates cracked, and the seams between plates simply opened up," Weihs says.

-- Johns Hopkins University Gazette, 26 April 1999

It would have sank even with perfect rivets!

[threaded]

Even if the rivets had been perfect it would still have sunk. The design was such that once a big enough hole was made, i.e. weren't enough pumps to keep the water level down, the water filled to above the bulkheads and swamped the next cell, and onto the next. It was a poor design when faced with the accident it had. IIRC the ships designer was on board and once he was told the size of the hole he was able to tell the captain how long it would take to sink.